Ceramic Bonding Interface under Shear–Compression Stress: Ultra-High-Speed Imaging Contribution - IMT Mines Alès Access content directly
Journal Articles Journal of Dental Research Year : 2023

Ceramic Bonding Interface under Shear–Compression Stress: Ultra-High-Speed Imaging Contribution

Abstract

The aim of this study is to visualize and characterize by ultra-high-speed imaging (UHSI) the failure phenomena at the resin–ceramic bonding interface of lithium disilicate (LiSi2) samples bonded with gold-standard protocol (Monobond Plus [MB]) and the nontoxic one (Monobond Etch & Prime [MEP]) subjected to mechanical loading. Unprecedented frame rate, image resolution, and recording time were reached by using the most advanced UHSI camera. The finite element analysis (FEA) of the proposed mechanical test confirmed that the specific design of our samples enables a combined shear and compression stress state, prone to test the bonding interface while being close to physiological stresses. Ten LiSi2 samples were pretreated by gold standard (MB, n = 5) and self-etching primer (MEP, n = 5). Axial compression loading gradually increased until catastrophic failure was performed. As shown by the FEA, the angle between the bonding interface and load direction leads to shear–compression stresses at the resin–ceramic bonding interface. Failure was recorded by UHSI at 300,000 fps. All recorded images were analyzed to segregate events and isolate the origin of fracture. For the first time, thanks to the image recording setup, it was observed that debonding is the first event before breakage, highlighting that sample fracture occurs by interfacial rupture followed by slippage and cohesive failure of materials. Failure mode could be described as mixed. MEP and MB showed similar results and behavior.
Fichier principal
Vignette du fichier
Lambert_al_J.Dental-Research_2023.pdf (1.47 Mo) Télécharger le fichier
Origin Files produced by the author(s)

Dates and versions

hal-03918312 , version 1 (06-01-2023)

Identifiers

Cite

Hugo Lambert, Stéphane Corn, Romain Léger, Patrick Ienny, Pierre Slangen, et al.. Ceramic Bonding Interface under Shear–Compression Stress: Ultra-High-Speed Imaging Contribution. Journal of Dental Research, 2023, 102 (3), pp.002203452211385. ⟨10.1177/00220345221138500⟩. ⟨hal-03918312⟩
77 View
143 Download

Altmetric

Share

Gmail Mastodon Facebook X LinkedIn More