The influence of montmorillonite on the flame‐retarding properties of intumescent bio‐based PLA composites - IMT Mines Alès Accéder directement au contenu
Article Dans Une Revue Journal of Applied Polymer Science Année : 2022

The influence of montmorillonite on the flame‐retarding properties of intumescent bio‐based PLA composites

Résumé

Biobased flame-retardant polylactic acid composites were prepared using ammonium polyphosphate (AP), lignin, and a raw montmorillonite (ANa) as the intumescent formulation. The concentration of AP and of ANa was varied in order to study its influence on the flammability properties of the composites. The samples were submitted to cone calorimeter test, thermogravimetric analysis coupled to Fourier-transform infrared spectroscopy (TGA-FTIR), limiting oxygen index (LOI), and UL-94 vertical burn. The cone calorimeter residues were analysed through scanning electronic microscopy, X-ray diffraction, and FTIR. The results show that the combined addition of the intumescent formulation and the ANa leads to an improvement in the fire behavior of the composites, compared with that of the neat polymer. The best fire-retardant performance was achieved by using the highest AP concentration (17%) and the lowest ANa concentration (1.2%), reaching a LOI value of 39%.
Fichier principal
Vignette du fichier
the-influence-of-montmorillonite.pdf (2.2 Mo) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-03590670 , version 1 (02-03-2022)

Identifiants

Citer

Raíssa Carvalho Martins, Simone Pereira da Silva Ribeiro, Regina Sandra Veiga Nascimento, Marco Antonio Chaer Nascimento, Marcos Batistella, et al.. The influence of montmorillonite on the flame‐retarding properties of intumescent bio‐based PLA composites. Journal of Applied Polymer Science, 2022, 139 (22), pp.52243. ⟨10.1002/app.52243⟩. ⟨hal-03590670⟩
45 Consultations
97 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More