Vieillissement hygrothermique des composites thermoplastiques renforcés par des fibres de verre – Partie II. Rôle de la matrice et de l’interface fibre/matrice sur les mécanismes de vieillissement des composites
Résumé
A study in an aggressive environment of the properties of short glass fibre rein_如ced thermoplastic composites based on poly (ethylene terephthalate), poly(butylene terephthalate) and polyamide-6,6 is reported. The influence of the fibre/matrix inte1face on
the composite behaviour in a moiety environment is especially studied hereby. Competitive phenomena may explain differences observed according with the nature of the fibre surface treatment. Among them these characteristics may be an intrinsic fragility of some chemical interfacial bondings, the hydrophilicity of some chemical groups, the presence of long macromolecular chains neighbouring the interface or of a transcristalline inte,facial area
Celle étude relate des propriétés en environnement agressif de composites thermoplastiques renforcés par des fibres de verre courtes à base de polyéthylène téréphtalate,et de polyamide-6,6. L'accent est porté en particulier sur le rôle de l'interface fibre/matrice sur le comportement des composites en milieu hygrothermique. L'existence d'une compétition entre plusieurs phénomènes peut expliquer les différences significatives observées selon la nature du traitement de surface des fibres. Ces caractéristiques sont, entre autres, la fragilité intrinsèque de certaines liaisons chimiques interfaciales, l'hydrophilie de certains groupements chimiques, la présence de longues chaînes macromoléculaires a l'interface ou d'une zone transcristalline interfaciale.
Origine | Fichiers produits par l'(les) auteur(s) |
---|