Effects of hygrothermal aging on chemical, physical, and mechanical properties of poly(3‐hydroxybutyrate‐co‐3‐hydroxyvalerate)/Cloisite 30B bionanocomposite - IMT Mines Alès Accéder directement au contenu
Article Dans Une Revue Polymer Composites Année : 2021

Effects of hygrothermal aging on chemical, physical, and mechanical properties of poly(3‐hydroxybutyrate‐co‐3‐hydroxyvalerate)/Cloisite 30B bionanocomposite

Résumé

Hygrothermal aging of neat poly(3‐hydroxybutyrate‐co‐3‐hydroxyvalerate) (PHBV) and PHBV filled with an organomodified montmorillonite (C30B) at 3wt. was investigated at 65°C and 100% relative humidity (RH) up to 100 days. FT‐IR data indicated that the carbonyl intensity index decreased with exposure time for both samples, while the main degradation mechanism occurred through hydrolysis reaction. This led to chain scissions resulting in a decrease in molar mass. Water absorption increased with exposure time for both neat PHBV and PHBV/C30B (3wt%) bionanocomposite. Differential scanning calorimetry measurements showed a decrease in both crystallinity index and melting temperature after hygrothermal aging and thermogravimetric analysis data indicated also a decrease in thermal stability. Mechanical and viscoelastic properties were also altered, being, however, more pronounced for the neat PHBV. Overall, the PHBV bionanocomposite exhibited a better resistance toward hygrothermal aging at 65°C and 100% RH.
Fichier principal
Vignette du fichier
effects-of-hygrothermal-aging.pdf (1.57 Mo) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-03113919 , version 1 (25-01-2021)

Identifiants

Citer

Kahina Iggui, Mustapha Kaci, Nicolas Le Moigne, Anne Bergeret. Effects of hygrothermal aging on chemical, physical, and mechanical properties of poly(3‐hydroxybutyrate‐co‐3‐hydroxyvalerate)/Cloisite 30B bionanocomposite. Polymer Composites, 2021, 42 (4), p.1878-1890. ⟨10.1002/pc.25943⟩. ⟨hal-03113919⟩
83 Consultations
193 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More