Under Glass Weathering of Hemp Fibers Reinforced Polypropylene Biocomposites: Degradation Mechanisms Based on Emitted Volatile Organic Compounds - IMT Mines Alès Accéder directement au contenu
Article Dans Une Revue Frontiers in Materials Année : 2020

Under Glass Weathering of Hemp Fibers Reinforced Polypropylene Biocomposites: Degradation Mechanisms Based on Emitted Volatile Organic Compounds

Résumé

The durability of hemp fibers reinforced polypropylene biocomposites was investigated after one year under glass exposure. Volatile organic compounds emissions were assessed using a new passive sampling method. Degradation pathways were examined in order to understand the weathering mechanisms. The polymer matrix was decomposed into oxygenated products due to UV rays and high temperatures. As regards hemp fibers, different degradation steps of the carbohydrates were highlighted according to the nature of the detected furans. At a non-weathered state, dehydrations preceded the ring-opening mechanism, often catalyzed by Maillard reactions. The further cyclization induced the formation of 2-or 5-substituted furans emitted by non-weathered materials. Reactions between identified products after weathering which were not yet found in literature were proposed in this paper. They often implied a keto-enol tautomerism but also dehydrations that induced the formation of 3-and 4-substituted furanones. These differences can be explained by a primary decomposition of carbohydrates favored at a non-weathered state and a secondary one occurring at a weathered state.

Domaines

Matériaux
Fichier principal
Vignette du fichier
Badji - 2020 - Under glass weathering of hemp MM biocomposites Degradation mechanisms based on VOC.pdf (1.99 Mo) Télécharger le fichier
2143d12ac3f77bf8cd7aaa5d5f0bfd8b9844.pdf (81.54 Ko) Télécharger le fichier
Origine : Fichiers éditeurs autorisés sur une archive ouverte
Commentaire : Corrigendum : Front. Mater., 06 November 2020, https://doi.org/10.3389/fmats.2020.00266

Dates et versions

hal-02873563 , version 1 (18-06-2020)

Identifiants

Citer

Célia Badji, Jean-Marc Sotiropoulos, J. Beigbeder, Hélène Garay, Anne Bergeret, et al.. Under Glass Weathering of Hemp Fibers Reinforced Polypropylene Biocomposites: Degradation Mechanisms Based on Emitted Volatile Organic Compounds. Frontiers in Materials, 2020, 7, ⟨10.3389/fmats.2020.00162⟩. ⟨hal-02873563⟩
148 Consultations
217 Téléchargements

Altmetric

Partager

Gmail Facebook Twitter LinkedIn More