Flame Retardant-Functionalized Cotton Cellulose Using Phosphonate-Based Ionic Liquids

Résumé

Cellulose from cotton fibers was functionalized through a dissolution-regeneration process with phosphonate-based ionic liquids (ILs): 1,3-dimethylimidazolium methylphosphonate [DIMIM][(MeO)(H)PO 2 ] and 1-ethyl-3-methylimidazolium methylphoshonate [EMIM][(MeO)(H)PO 2 ]. The chemical modification of cellulose occurred through a transesterification reaction between the methyl phosphonate function of ILs and the primary alcohol functions of cellulose. The resulting cellulose structure and the amount of grafted phosphorus were then investigated by X-ray diffraction, ICP-AES, and 13 C and 31 P NMR spectroscopy. Depending on the IL type and initial cotton / IL ratio in the solution, regenerated cellulose contained up to 4.5% of phosphorus. The rheological behavior of cotton cellulose/ILs solutions and the microscale fire performances of modified cellulose were studied in order to ultimately prepare flame retardant cellulosic materials. Significant improvement in the flame retardancy of regenerated cellulose was obtained with a reduction of THR values down to about 5-6 kJ/g and an increase of char up to about 35 wt%.
Fichier principal
Vignette du fichier
molecules-25-01629.pdf (18.2 Mo) Télécharger le fichier
Origine : Fichiers éditeurs autorisés sur une archive ouverte
Loading...

Dates et versions

hal-02537288 , version 1 (08-04-2020)

Identifiants

Citer

Karen Al Hokayem, Roland El Hage, Lenka Svecova, Belkacem Otazaghine, Nicolas Le Moigne, et al.. Flame Retardant-Functionalized Cotton Cellulose Using Phosphonate-Based Ionic Liquids. Molecules, 2020, 25 (7), pp.1629. ⟨10.3390/molecules25071629⟩. ⟨hal-02537288⟩
125 Consultations
152 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More